Our site saves small pieces of text information (cookies) on your device in order to deliver better content and for statistical purposes. You can disable the usage of cookies by changing the settings of your browser. By browsing our site without changing the browser settings you grant us permission to store that information on your device.

I agree, do not show this message again.

Structure – properties relationships in Ce-doped lead titanate ceramics

E. DIMITRIU1,2, R. RAMER3,* , F. CRACIUN4, G. PRODAN2, V. CIUPINA2

Affiliation

  1. REGO COM, Calea 13 Septembrie 115, Bucharest, Romania
  2. Interdisciplinary Research Institute for Micro and Nanostructures, University Ovidius”, Bd. Mamaia 124, Constanta, Romania
  3. School of Electrical Engineering and Telecommunications, University of South Wales, Sydney 2052, Australia
  4. CNR Istituto dei Sistemi Complessi, Area di Ricerca Tor Vergata, Via del Fosso Cavaliere 100, 00133 Roma, Italy

Abstract

The interest on the materials containing CeO2 has increased due to the ability of CeO2 to undergo rapid redox cycles. The oxygen partial pressure and the presence of cations with a lower oxidation state influence the reduction behaviour of CeO2. This work reports a comparative study on microstructure, dielectric and piezoelectric properties of Ce- and Ce, Eu doped lead titanate ceramics. The samples with a complex composition were prepared by solid-state reaction of oxide and carbonate powders. Substitutions of Ce4+ and Ce4+, Eu3+ for Pb2+, and Mn4+ for Ti4+ were performed. Nanostructured materials with tetragonal perovskite phase were revealed and investigated by high-resolution transmission electron microscopy (HRTEM), selected area electron diffraction (SAED) and X-ray diffraction. The local distribution of the chemical elements was revealed using the wavelength dispersive spectroscopy. The porosity of the ceramics was also investigated. Dielectric permittivity was measured in a wide temperature and frequency range. The temperature dependence of the piezoelectric properties is reported. It is found that the substitution of Eu3+ for Ce4+ improves the piezoelectric properties of the PT-type ceramics..

Keywords

Piezoceramics, Lead titanate, Rare earth, Electromechanical properties, Microstructure.

Submitted at: Oct. 14, 2005
Accepted at: Jan. 26, 2006

Citation

E. DIMITRIU, R. RAMER, F. CRACIUN, G. PRODAN, V. CIUPINA, Structure – properties relationships in Ce-doped lead titanate ceramics, Journal of Optoelectronics and Advanced Materials Vol. 8, Iss. 1, pp. 55-59 (2006)