Our site saves small pieces of text information (cookies) on your device in order to deliver better content and for statistical purposes. You can disable the usage of cookies by changing the settings of your browser. By browsing our site without changing the browser settings you grant us permission to store that information on your device.I agree, do not show this message again.
JAN JARGUS1, JAN NEDOMA1,* , RADEK MARTINEK2
- Department of Telecommunications, Faculty of Electrical Engineering and Computer Science, VSB - Technical University of Ostrava, 17. listopadu 15/2172, 708 33 Ostrava, Czech Republic
- Department of Cybernetics and Biomedical Engineering, Faculty f Electrical Engineering and Computer Science, VSB - Technical University of Ostrava, 17. listopadu 15/2172, 708 33 Ostrava, Czech Republ
This paper examines how the variable excitation wavelength affects CCT (correlated colour temperature) and CRI (colour rendering index) of the light generated by the luminescent layer. Two types of samples with a defined layer thickness and with a defined weight ratio of the YAG:Ce (cerium-doped yttrium aluminium) phosphor in PDMS (polydimethylsiloxane) were used. The measurements were performed in the wavelength range from 440 nm to 470 nm. The measurement results indicate that by using a suitable excitation wavelength and a suitable phosphor weight ratio in a luminescent layer of a defined thickness, the CCT and CRI parameters can be optimized..
CRI, CCT, PDMS, Spectral characteristic, YAG:Ce phosphor.
Submitted at: Aug. 7, 2018
Accepted at: June 14, 2019
JAN JARGUS, JAN NEDOMA, RADEK MARTINEK, Dependence of CCT and CRI on the variable excitation wavelength and on the weight ratio of the phosphor in polydimethylsiloxane, Journal of Optoelectronics and Advanced Materials Vol. 21, Iss. 5-6, pp. 327-332 (2019)
- Download Fulltext
- Downloads: 101 (from 71 distinct Internet Addresses ).