Our site saves small pieces of text information (cookies) on your device in order to deliver better content and for statistical purposes. You can disable the usage of cookies by changing the settings of your browser. By browsing our site without changing the browser settings you grant us permission to store that information on your device.I agree, do not show this message again.
A. MATEI1,* , V. ȚUCUREANU1,2, B. C. ŢÎNCU1,3, M. AVRAM1, C. ROMANIȚAN1,4, M. C. POPESCU1
- National Institute for Research and Development in Microtehnologies Bucharest, 126A, Erou Iancu Nicolae Street, 077190, Romania
- Transilvania University of Brasov, Department of Materials Science, 29, B-dul Eroilor, 500036, Romania
- University Politehnica of Bucharest, Faculty of Applied Chemistry and Materials Science, 1-7 Polizu, 011061 Bucharest, Romania
- Faculty of Physics, University of Bucharest, 405 Atomistilor Street, 077125, Magurele, Romania
The main purpose of the paper is to study the behavior of the Y2O3 filler in the PVDF matrix and the use of materials synthesized as coating films. For the nanocomposites synthesis, in the incipient phase the polymer solution is obtained by dissolving the polymer in the corresponding solvent. Thus, composites were obtained by mixing the main components, followed by the ultrasonication step in order to obtain a well-dispersed solution and deposited on unconventional substrates. After deposition, the film was thermally treated at 80°C in order to remove the solvent and to densify the synthesized material. The impact of Y2O3 filler on the morphological and structural properties of the matrix was investigated by FTIR, XRD, FE-SEM, EDX and contact angle. From the FTIR spectra analysis of the composite the presence of characteristic bands of the α and β phase was observed. The XRD spectra indicate that the addition of the Y2O3 did not modify the PVDF structure. SEM analysis shows that Y2O3 particles are embedded in the matrix, and the interaction between the components has led to particle size growth through a slight agglomeration tendency. EDX spectra of the composite indicate the presence of the two components, the contact angle show the improvement of hydrophobic character of the nanocomposite film..
Y2O3, PVDF, Nanocomposites.
Submitted at: Jan. 7, 2019
Accepted at: Aug. 20, 2019
A. MATEI, V. ȚUCUREANU, B. C. ŢÎNCU, M. AVRAM, C. ROMANIȚAN, M. C. POPESCU, Enhancement of nanocomposite materials properties based on Y2O3 filler and PVDF matrix, Journal of Optoelectronics and Advanced Materials Vol. 21, Iss. 7-8, pp. 541-546 (2019)