Our site saves small pieces of text information (cookies) on your device in order to deliver better content and for statistical purposes. You can disable the usage of cookies by changing the settings of your browser. By browsing our site without changing the browser settings you grant us permission to store that information on your device.

I agree, do not show this message again.

High density MgB2 superconductor: structure and morphology through microtomography and SEM investigations

GH. –V. ALDICA1,* , P. NITA2, I. TISEANU3, T. CRACIUNESCU3, P. BADICA1

Affiliation

  1. National Institute of Materials Physics, Bucharest-Magurele, Romania
  2. METAV SA, Bucharest, Romania
  3. National Institute for Lasers, Plasma and Radiation Physics, Bucharest-Magurele, Romania

Abstract

Recently, MgB2 was discovered to be a superconductor with a surprisingly high critical temperature of about 39 K and with significant potential for applications. This material is usually prepared from a mixture of Mg and B in sealed tubes with excess Mg. As-prepared samples usually are very porous and mechanically weak. High density superconducting samples of MgB2 undoped and doped with SiC and B4C were produced by Field Assisted Sintering Technique (FAST) (Tc = 38.5 K). Samples are relatively large of 1.9 cm in diameter, apparently uniform, and can be easily extracted from the die. Processing times are short for easily attainable and relatively low temperatures. The effects of FAST consolidation on crystalline morphology revealed by microtomography and Scanning Electron Microscopy (SEM) and bulk density were investigated. Most samples have bulk density above 90% of the theoretical one. Despite such high bulk density, microtomography in combination with SEM revealed that in the samples there are some regions of low and high density. High density regions are not the consequence of FAST processing and they were observed in the raw material..

Keywords

SEM, X-ray μ-tomography, MgB2 superconductor, Microstructure.