Our site saves small pieces of text information (cookies) on your device in order to deliver better content and for statistical purposes. You can disable the usage of cookies by changing the settings of your browser. By browsing our site without changing the browser settings you grant us permission to store that information on your device.

I agree, do not show this message again.

Low-cycle fatigue of an aluminum alloy plated with multi-layered deposits

Ya. B. UNIGOVSKI1,* , A. GRINBERG1, E. GERAFI1, E. M. GUTMAN1, S. MOISA1

Affiliation

  1. Ben-Gurion University of the Negev, Department of Materials Engineering, Beer-Sheva, Israel

Abstract

Low-cycle fatigue (LCF) in engineering structures is caused by a relatively low-frequency strain cycling or thermal cycling. Regardless of the fact that it is much more dangerous than high-cycle fatigue, it has not been studied enough. Coated aluminum alloys are widely used in aerospace and transportation industries, mostly because of their high toughness and strength-weight ratio and improved surface properties. The effect of one-, two- and three-layer coatings, including an inner electroless nickel layer and, additionally, electrodeposited nickel, gold and silver, on the LCF behavior of 1.6-mm-thick 6061-T6 Al alloy was studied in a strain-controlled purely bending mode. The lifetime of the coated alloy drastically decreases as compared to the substrate. The incipient cracks were revealed, first of all, in the electroless nickel layer and in the substrate close to its surface..

Keywords

Low-cycle fatigue, Coated aluminum alloy, Deposit thickness.