Our site saves small pieces of text information (cookies) on your device in order to deliver better content and for statistical purposes. You can disable the usage of cookies by changing the settings of your browser. By browsing our site without changing the browser settings you grant us permission to store that information on your device.I agree, do not show this message again.
Y. ACİKBAS1, R. CAPAN2, F. YUKRUK3, M. ERDOGAN2
- Department of Material Science and Nanotechnology Engineering, Faculty of Engineering, University of Usak, Turkey
- Department of Physics, Faculty of Science, University of Balikesir, Turkey
- Department of Chemistry, Faculty of Science, University of Balikesir, Turkey
The Langmuir–Blodgett (LB) technique was employed to produce thin LB films using N,N’-(glycine tert-butylester)-3,4,9,10- perylenediimide (FY1) material on gold coated glass. The characteristics of the perylenediimide FY1 LB films are assessed by surface plasmon resonance (SPR) measurements. The experimental SPR data are fitted using the Winspall software to evaluate the film thickness and refractive index of this material. Thickness of LB films were determined to be 0.66±0.07 nm per monolayer of FY1, and the refractive index value of FY1 was obtained as 1.41±0.06. FY1 LB thin film sensor element was exposed to chloroform, benzene and toluene vapors. Results show that the response of the FY1 film to chloroform was the largest among organic vapors with the photodetector response change, ∆Irf value of 0.082 au. It can be proposed that these LB films have good sensitivity and selectivity for saturated chloroform vapor..
Perylenediimide, Optical properties, SPR; Langmuir-Blodgett thin films, Sensors.
Submitted at: April 15, 2015
Accepted at: Sept. 29, 2016
Y. ACİKBAS, R. CAPAN, F. YUKRUK, M. ERDOGAN, Optical characterization and organic vapor sensing application of perylendiimide Langmuir-Blodgett thin films, Journal of Optoelectronics and Advanced Materials Vol. 18, Iss. 9-10, pp. 832-836 (2016)