Our site saves small pieces of text information (cookies) on your device in order to deliver better content and for statistical purposes. You can disable the usage of cookies by changing the settings of your browser. By browsing our site without changing the browser settings you grant us permission to store that information on your device.I agree, do not show this message again.
Y. ZHANG1, M. RUAN1, Q. ZHOU1, X. MU1, J. DU1, E. XIE1, Y. SHENG1,* , Z. ZHANG1
- School of Physical Science and Technology, Lanzhou University, Lanzhou 730000, PR China
Molybdenum trioxide (MoO3) powders have been prepared with controllable Eu concentrations (1~7 at. %). The X-ray diffraction and Raman results show MoO3 belongs to the orthorhombic phase. The intense sharp characteristic emission lines corresponding to Eu3+ intra-4f shell transitions of MoO3 were observed in the photoluminescence emission spectra at room temperature and exhibited a maximum at the 3 at. % Eu sample. The optical bandgap of MoO3 decreases from 3.26 to 3.14 eV as the Eu doping concentration increases from 1% to 7 at. %. Moreover, an energy transfer mechanism from MoO3 host to Eu3+ ions is proposed..
Molybdenum trioxide, Optical materials and properties, Sintering, Energy transfer, Rare earths.
Submitted at: April 23, 2018
Accepted at: Nov. 29, 2018
Y. ZHANG, M. RUAN, Q. ZHOU, X. MU, J. DU, E. XIE, Y. SHENG, Z. ZHANG, Photoluminescence mechanism of Eu-doped molybdenum trioxide prepared by combustion synthesis, Journal of Optoelectronics and Advanced Materials Vol. 20, Iss. 11-12, pp. 642-645 (2018)