Our site saves small pieces of text information (cookies) on your device in order to deliver better content and for statistical purposes. You can disable the usage of cookies by changing the settings of your browser. By browsing our site without changing the browser settings you grant us permission to store that information on your device.

I agree, do not show this message again.

Synthesis and characterization of nobles metals nanowires

O. G. DRAGOŞ1,* , H. CHIRIAC,1, C. GHERASIM1, N. LUPU1

Affiliation

  1. National Institute of Research & Development for Technical Physics, 47 Mangeron Boulevard Iaşi, RO-700050, România

Abstract

Large-scale Pt, Au, Ag nanowires were successfully synthesized by using pulsed electrodeposition within the anodic alumina oxide (AAO) templates. The diameter and length of as-obtained nanowires were approximately 200 nm and 50 μm, respectively, corresponding to the pore sizes and thickness of AAO templates. The morphologies, microstructures, compositions, and electric proprieties of the as-synthesized nanowires were systematically investigated by SEM, EDS, and I – AFM analysis.

Keywords

Electrodeposition, Gold, silver, Platinum, Nanowires, I-AFM.