Our site saves small pieces of text information (cookies) on your device in order to deliver better content and for statistical purposes. You can disable the usage of cookies by changing the settings of your browser. By browsing our site without changing the browser settings you grant us permission to store that information on your device.

I agree, do not show this message again.

X-ray diffraction analysis of PbTe/SnTe superlattices grown on Si(111) substrates

O. SHAPOVAL1, A. BELENCHUK1, A. FEDOROV2, V. KANTSER1, E. ZASAVITSKY1,*

Affiliation

  1. Institute of Electronic Engineering and Industrial Technologies, ASM, 3/3 Acdemiei str., 2028 Chisinau, Moldova
  2. Institute of Single Crystal, NASU, 60 Lenin ave., 61001 Kharkov, Ukraine

Abstract

The 50 period PbTe/SnTe superlattices (SLs) were grown on Si (111) substrates by hot-wall beam epitaxy (HWBE) using an intermediate fluoride buffer. The SL period varied from 6.6 to 24.0 nm with PbTe:SnTe thickness ratios of 2:1 and 1:1. The structural analysis was performed by X-ray diffraction and reflection measurement techniques. The resolution up to 8 orders of SL satellite diffraction peaks indicates well-formed SLs with sharp interfaces and long range ordering. The processing of X-ray spectra on the basis of dynamical theory of diffraction was used for estimation of individual layer thicknesses and residual strains. The differences in lattice parameters both between SL components and relative to the substrate, as well as the thermal expansion coefficient mismatch of A4 B6 compounds with regard to the substrate, are the reasons for the strains appearing in this SL structure. Fitted parameters of the normal lattice mismatch revealed that the SnTe layers are equally strained independent of thickness, whereas the stress of PbTe layers is progressively decreasing with thickness. In spite of residual lattice mismatch strain, the SL structures exhibited ability to full relax of the thermal mismatch strains as in the case of earlier investigated single layers of A4 B6 grown on Si (111) coated with fluoride buffer. Our results indicate the possibility to fabricate high efficient thermoelectric coolers based on PbTe/SnTe SLs directly integrated with Si chips..

Keywords

PbTe, SnTe, Superlattice, Si substrate, Fluoride buffer, X-ray diffraction, Simulation, Strain relaxation.